Yeah man. Sorry about the distinct lack of visual aids. I will pop some up tonight.
I have varnished it last night using an exterior matte varnish. Matte anything is OK in my books. Looks nice. Flawed but nice.
Looks like we might get some turns in later in the month. Woo.
Search found 121 matches
- Thu Aug 08, 2013 1:56 am
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
- Tue Aug 06, 2013 12:12 pm
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
- Sun Aug 04, 2013 12:11 am
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
We will see chrismp, we will see :) I think I may have spoiled my epoxy by putting the hardener lid on the epoxy and the other way round when I seated in the t nuts. The epoxy was lumpier than I remembered it. It seems crazy that such a little amount of hardener that could have sat on the lid could ...
- Sat Aug 03, 2013 10:16 pm
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
hey guys So my skim coat didn't really become drier after a week. Today I went to bunnings and got myself a heat gun and some other goodies and have taken to the board. I have gotten 99 percent of the goop off and feel better now. I have also trimmed and routed the sidewalls after giving them a belt...
- Thu Aug 01, 2013 2:02 pm
- Forum: Journals: Log Your Ski Building Progress
- Topic: OAC 2013/2014
- Replies: 27
- Views: 19345
- Mon Jul 29, 2013 1:13 pm
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
- Mon Jul 29, 2013 3:00 am
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
Domo Arigato Gozaimaaaaass. I used the entropy that doesn't need heat so I thought it would be ok. I had another look today and it looks like it's slowly hardening. I have used a scraper to see if I can scrape some of the tacky stuff off in one patch and have scuffed it up on another. I am going to ...
- Sun Jul 28, 2013 1:02 am
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
- Sat Jul 27, 2013 11:36 pm
- Forum: Journals: Log Your Ski Building Progress
- Topic: David's yet to be named thread
- Replies: 80
- Views: 51001
Hey Guys, So I had a crack at pressing my first board on Friday. I am not sure I would have called it a success. It seems kinda like it worked. So I layed everything up and it looked like it was going well. The problem came when I tried to bag it up. I hadn't put a layer of plastic under the board t...
- Mon Jul 08, 2013 4:43 pm
- Forum: Materials and Supplies
- Topic: split ends
- Replies: 13
- Views: 8032
- Mon Jul 08, 2013 12:12 pm
- Forum: Materials and Supplies
- Topic: split ends
- Replies: 13
- Views: 8032
- Wed Jun 26, 2013 12:07 am
- Forum: Materials and Supplies
- Topic: mastic tape
- Replies: 7
- Views: 5878
- Tue Jun 25, 2013 1:59 pm
- Forum: Materials and Supplies
- Topic: mastic tape
- Replies: 7
- Views: 5878
mastic tape
Hi folks, I have been trying to find some mastic tape to seal when vacuum bagging. Everywhere I go people look at me like I am speaking some strange language when I ask for it here in Australia. Does anyone know what other names it could be called or what its originally designed to do? Any other sug...
- Mon Jun 03, 2013 11:48 pm
- Forum: Materials and Supplies
- Topic: split ends
- Replies: 13
- Views: 8032
- Mon Jun 03, 2013 1:54 pm
- Forum: Materials and Supplies
- Topic: split ends
- Replies: 13
- Views: 8032
split ends
Hi everyone,
Quick question. My cores crack/split quite easily along the grain in the tip and tail. They are 2mm thick. I am guessing as long as I keep it flat when pressing the epoxy will fix this up? Incorrect? Thoughts?
Quick question. My cores crack/split quite easily along the grain in the tip and tail. They are 2mm thick. I am guessing as long as I keep it flat when pressing the epoxy will fix this up? Incorrect? Thoughts?